Oxidation of porous nanocrystalline titanium nitride. II. Scale structure and composition

We have used x-ray phase analysis to study the composition of the products of reaction between oxygen and nanocrystalline powders with particle sizes 15, 40, 55, and 80 nm, and also specimens pressed (and sintered) from them. The powders were oxidized in air at 100°C (400 h) to 500°C (5 min), while the sintered specimens were oxidized at 600–900°C for 15, 120, and 240 min. In all cases, in the initial oxidation step the oxynitride Ti(O_xN_y) is formed, which over time is oxidized to TiO, Ti₂O₃, Ti₃O₅, TiO₂ (anatase) and TiO₂ (rutile). In the range 600–800°C, formation of a continuous oxide layer and conversion of anatase to rutile slows down diffusion of oxygen in the scale. We have established that at 900°C, the growth rate of the scale thickness increases and so the reflections from the oxynitride are barely noticeable on the diffraction patterns taken from the surface of the oxidized specimen. In these diffraction patterns, along with strong reflections from the rutile, we also observed weak reflections from lower oxides and anatase, which may be due to reaction between oxygen and the titanium ions diffused to the scale surface. We have concluded that at T > 850°C, the mechanism for oxidation of TiN changes. This is due to superposition of counterdiffusion of titanium ions on the diffusion of oxygen. __________ Translated from Poroshkovaya Metallurgiya, Nos. 3–4(448), pp. 72–78, March–April, 2006.     

钛铁矿流态化氧化机理研究

对低品位钛铁矿进行预氧化、预还原等预处理后可满足硫酸法生产钛白粉工艺所需高品位钛铁矿的要求。本试验采用流态化预氧化方法处理风化程度低、含硫较高的钛铁矿。结果表明 :流态化氧化可大幅度地降低钛铁矿中硫含量 ;钛铁矿流态化氧化的适宜温度为 :80 0～ 90 0℃ ,且在此温度范围内 ,随温度的升高 ,钛铁矿的氧化速度增加 ,在 90 0℃时 ,5 0min钛铁矿基本能完成氧化     

单壁纳米碳管/纳米铝基复合材料的增强效果

用半连续氢电弧法和活性氢等离子蒸发法分别制备出单壁纳米碳管(SWNTs)和纳米A1粉体，然后用提纯后的SWNTs和纳米A1粉体制备出SWNTs含量(质量分数)分别为0、2．5％、5．0％、7．5％和10.0％的单壁纳米碳管／纳米铝基块体复合材料．SWNTs对高强度纳米A1基体具有显著的增强作用，当SWNTs含量小于5．0％时，材料的硬度随着SWNTs含量的提高线性上升．其中5％SWNTs和纳米A1的复合增强效果最好，其硬度可达2.89GPa，大约是粗晶A1(0．15GPa)的20倍．当SWNTs含量超过5．0％时，增强效果开始缓慢的下降．讨论了单壁纳米碳管增强纳米铝基复合材料的强化机制．     

Preparation of Compound Ultrafine CeO2 by Wet-Solid-Phase Mechanochemical Modification

To satisfy practical requirements from industrial applications, an alternate route for synthesis compound ultrafine CeO2 powders by wet-solid-phase mechanochemical modification using industrial grade hydrated cerium carbonate as raw material was proposed.The effect of modifier reaction percentage, reaction time, calcining temperature and modifier amount on particle size, density, suspensibility, and hardness of compound CeO2 powder was investigated.The phase evolutions of preparation process were characterized by XRD.SEM micrograph of the final product shows that compound CeO2 powders obtained are well-dispersed, spherically-shaped, uniformly-sized and submicron-sized particles.The method is readily available in raw material, low in cost, simple in process, and has great potential for industrialization.The compound CeO2 powders of different physical properties can be synthesized by controlling the above-mentioned influence factors in preparation process.     

高压水射流技术粉碎原盐的研究

以原盐为被粉碎研究对象,通过对高压水射流粉碎原盐形貌的观察和成分分析、高压水射流原盐粉碎性能分析,以及高压水射流粉碎原盐各影响因素的正交分析,研究表明高压水射流粉碎技术对原盐具有良好的解理性且粉碎效率高、耗能低。各因素对原盐粉碎效果的影响顺序为:射流压力卤水喷嘴直径、料液混合喷嘴直径、靶面形状。     

汽轮机轴承烧瓦与轴颈的渗巴氏合金现象

简述轴承工作性质，巴氏合金应用与相组成的基本情况。论述汽轮机转子在两个电厂长期运行后，由于轴颈发生的不正常摩擦损伤，在大修改造中由无损检查、机械加工揭示出轴颈存在严重的渗巴氏合金现象，低熔点金属Sn、Sb与Cu向转子材料晶界的深层渗入最终导致了3根大型在投转子的严重开裂与报废。图11表2     

低松装密度水雾化铜粉工艺的研究

本文研究了氧化 还原法生产铜粉的新工艺 ,该工艺是通过氧化还原将水雾化铜粉加以表面改性 ,形成海绵状的粉末 ,显著降低水雾化铜粉的松装密度 ,这种铜粉既具有电解铜粉低的松装密度 ,又具有水雾化铜粉高的流动性。讨论了氧化时间、氧化温度对铜粉松装密度的影响。本工艺是一种新型环保、节能、可替代电解法生产铜粉的先进工艺     

W-Ni-Cu高比重合金注射成形烧结收缩及性能的研究

研究了W-Ni-Cu高比重合金注射成形工艺过程收缩率和性能。比较了模具尺寸、注射坯尺寸、烧结坯尺寸，及烧结阶段各方向收缩率的关系，发现实际收缩与理论预测收缩率较为一致，但在厚度方向存在与其他方向收缩不一致的情形，这与由重力作用产生的塑料流动有关；还探讨了烧结坯密度与烧结条件的关系，测定了烧结坯的力学性能及断口形貌、金相组织，烧结坯在1400℃，90min烧结达到了99％的相对密度，断裂强度600MPa以上。     

光敏树脂及其紫外光固化涂料发展新动向

按紫外光固化涂料形态分类,并着重从光敏树脂方面综述了近年来紫外光固化涂料及其光敏研究及开发的新动向。在开发油性紫外光固化涂料新品种、提高其综合性能、拓宽应用领域的同时,研究开发水性紫外光固化涂料、紫外光固化粉沫涂料是目前紫外光固化涂料的重要发展趋向:在完善线形光敏齐聚物的同时,研究水溶性光敏齐聚物、树枝形和超支化结构聚合物体系又成为紫外光固化涂料用树脂研究的新热点。     

低熔融指数聚丙烯的开发生产

总结了开发生产低熔融指数聚丙烯的试验过程与结果，通过优选催化剂、优化操作过程、控制加氢量，生产出质量稳定可靠的熔融指数在0．2～0．5g/l0min之间的低熔融指数聚丙烯．